Izgradnja |
| ||||
Nominal Diameter | Približna težina | Minimalno prekidno opterećenje koje odgovara razredu užeta od | |||
1570 | 1670 | 1770 | 1870 | ||
MM | KG/100M | KN | KN | KN | KN |
0.5 | 0,125 | - | 0,255 | - | - |
1 | 0.5 | - | 1 | - | - |
1.5 | 1.125 | 1.9 |
| 2.15 | 2.27 |
2 | 2 | 3.63 |
| 4.11 | 4.35 |
2.5 |
| 4.88 | 5.19 | 5.5 | 5.81 |
3 | 4.5 | 7.63 | 8.11 | 8.6 | 9.08 |
4 | 8 | 12.8 | 13.7 | 14.5 | 15.3 |
5 | 12.5 | 19.5 | 20.7 | 22 | 23.2 |
6 | 18 | 30.5 | 32.4 | 34.4 | 36.3 |
7 | 24.5 | 43.9 | 46.7 | 49.5 | 52.3 |
8 | 32 | 51.5 | 54.8 | 58.1 | 61.4 |
9 | 40.5 | 68.6 | 73 | 77.4 | 81.7 |
10 | 50 | 93.4 | 99.4 | 105 | 111 |
11 |
| 112 | 119 | 126 | 1333 |
12 | 72 | 122 | 129 | 137 | 145 |
Izgradnja | |||||
Nominal Diameter | Približna težina | Minimalno prekidno opterećenje koje odgovara razredu užeta od | |||
1570 | 1670 | 1770 | 1870 | ||
MM | KG/100M | KN | KN | KN | KN |
1 | 0,51 | 0,83 | 0.88 | 0,93 | 0,99 |
1.5 |
| 1.87 | 1.99 | 2.11 | 2.22 |
2 | 2.03 | 3.32 | 3.54 | 3.75 | 3.96 |
2.5 | 3.17 | 5.2 | 5.53 | 5.86 | 6.19 |
3 | 4.56 | 7.48 | 7.96 | 8.44 | 8.91 |
4 | 8.12 | 13.3 | 14.1 | 15 | 15.8 |
5 | 12.68 | 20.8 | 22.1 | 23.4 | 24.7 |
6 | 18.26 | 29.9 | 31.8 | 33.7 |
|
7 | 24.85 | 40.7 | 43.3 | 45.9 | 48.5 |
8 | 32.45 | 53.2 | 56.6 | 60 | 63.4 |
9 | 41.07 | 67.4 | 71.6 | 75.9 | 80.2 |
10 | 50.71 | 83.2 | 88.5 |
| 99.1 |
11 | 61.36 | 100 | 107 | 113 | 119 |
12 | 73.02 | 119 | 127 | 135 | 142 |
Izgradnja | ||||||||||
Nominal Diameter | Približna težina | Minimalno prekidno opterećenje koje odgovara razredu užeta od | ||||||||
Fiber Core | Čelična jezgra | 1570 | 1670 | 1770 | 1870 | |||||
FC | IWS | FC | IWS | FC | IWS | FC | IWS | FC | IWS | |
MM | KG/100M | KN |
|
|
|
|
|
|
|
|
1.5 | 0,83 | 0,81 | 1.12 | 1.31 | 1.19 | 1.39 | 1.26 | 1.47 | 1.33 | 1.56 |
2 | 1.48 | 1.44 | 1.99 | 2.33 | 2.12 | 2,47 | 2.25 | 2.62 | 2.38 | 2.77 |
2.5 | 2.31 | 2.25 | 3.12 | 3.64 | 3.32 |
| 3.51 | 4.1 | 3.71 | 4.33 |
3 | 3.32 | 3.24 | 4.49 | 5.24 | 4.78 | 5.57 | 5.06 | 5.91 | 5.35 | 6.24 |
4 | 5.9 | 5.76 | 7.99 | 9.32 | 8.5 | 9.91 | 9.01 | 10.51 | 9.52 | 11.1 |
5 | 9.23 | 9 | 12.48 | 14.57 | 13.28 | 15.49 | 14.07 | 16.42 | 14.87 | 17.35 |
6 | 13.3 | 13 | 18.6 | 20.1 | 19.8 | 21.4 | 21 | 22.6 | 22.2 | 23.9 |
8 | 23.6 | 23 | 33.1 | 35.7 | 35.2 | 38 | 37.3 | 40.3 | 39.4 | 42.6 |
10 | 36.9 | 36 | 51.8 | 55.8 | 55.1 | 59.4 | 58.4 | 63 | 61.7 | 66.5 |
12 | 53.1 | 51.8 | 74.6 | 80.4 | 79.3 | 85.6 | 84.1 |
| 88,8 | 95.8 |
14 | 72.2 | 70.5 | 101 | 109 | 108 | 116 | 114 | 123 | 120 | 130 |
16 | 94.4 | 92.1 | 132 | 143 | 141 | 152 | 149 | 161 | 157 | 170 |
18 | 119 | 117 | 167 | 181 | 178 | 192 | 189 | 204 | 199 | 215 |
20 | 147 | 144 | 207 | 223 | 220 | 237 | 233 | 252 | 246 | 266 |
Izgradnja | ||||||||||
Nominal Diameter | Približna težina | Minimalno prekidno opterećenje koje odgovara razredu užeta od | ||||||||
Fiber Core | Čelična jezgra | 1570 | 1670 | 1770 | 1870 | |||||
FC | IWS | FC | IWS | FC | IWS | FC | IWS | FC | IWS | |
MM | KG/100M | KN | ||||||||
0.5 | 0,092 | 0.09 | 0,127 |
| 0.135 | 0,158 | 0.144 | 0.168 | 0,152 | 0,177 |
1 | 0.367 | 0.36 | 0.511 | 0.596 | 0.543 | 0.634 | 0,576 | 0,672 | 0.608 | 0,71 |
1.5 |
| 0,81 | 1.15 | 1.34 | 1.22 | 1.42 | 1.29 | 1.51 |
| 1,59 |
2 | 1.47 | 1.44 | 2.08 | 2.25 |
| 2.39 | 2.35 | 2.54 | 2.48 | 2.68 |
3 | 3.3 | 3.24 | 4.69 | 5.07 | 4.98 | 5.39 |
| 5.71 | 5.58 | 6.04 |
4 | 5.88 | 5.76 | 8.33 | 9.01 | 8.87 | 9.59 | 9.4 | 10.1 | 9.93 | 10.7 |
5 | 9.18 | 9 | 13 | 14 | 13.8 | 14.9 | 14.6 | 15.8 | 15.5 | 16.7 |
6 | 13.22 | 12.96 | 18.7 | 20.2 | 19.9 | 21.5 | 21.1 | 22.8 | 22.3 | 24.1 |
8 | 23.5 | 23.04 | 33.3 | 36 | 35.4 | 38.3 | 37.6 |
| 39.7 | 42.9 |
10 | 36.72 | 36 | 52.1 | 56.3 | 55.4 | 59.9 | 58.7 | 63.5 | 62 | 67.1 |
12 | 52.88 | 51.84 | 75 | 81.1 | 79.8 | 86.3 | 84.6 | 91.5 | 89.4 | 96.6 |
1. Nemojte koristiti novo uže od nehrđajućeg čelika direktno pri velikoj brzini i velikom opterećenju
Novo uže od nehrđajućeg čelika ne treba koristiti direktno pri velikoj brzini i velikom opterećenju, već treba raditi neko vrijeme pod uvjetima male brzine i srednjeg opterećenja.Nakon što je novi konopac prilagođen stanju upotrebe, a zatim postepeno povećavajte brzinu rada žičane konopce i opterećenja podizanja.
2.Tepano od nehrđajućeg čelika ne može se isključiti iz utora
Kada se žičano uže od nehrđajućeg čelika koristi s koloturom, obratite pažnju da se užad za užad ne može odvojiti od žljeba remenice.Ako žičani konop i dalje koristi nakon pada utora za remenicu, žičani konopac će biti stisnut i deformiran, kinkd, slomljen i slomljeni pramce, koji će ozbiljno skratiti radni vijek žičane konopce.Ako konopac pukne, to će često donijeti teške posljedice.
3. Nemojte pritiskati uže od nehrđajućeg čelika
Nehrđajući čelični konop ne smije se snažno pritisnuti kako bi se izbjegla deformacija tijekom upotrebe ili će dovesti do žičane loma, pramene ili čak lom u konopu, koji će skratiti radni vijek žičane konopce i ugroziti operativnu sigurnost.
4. Nemojte trljati ostalim predmetima kada se užad od nehrđajućeg čelika radi pri velikom brzinom
Kada žičano uže od nehrđajućeg čelika radi velikom brzinom, trenje između užeta od nehrđajućeg čelika i predmeta izvan utora kotača je glavni razlog ranog kidanja žice.
5.Ne nasumično vjetrajte nehrđajućeg čelika
Kada je inox žičano uže namotano na bubanj, treba ga rasporediti što je moguće urednije.Ili će čelični konop biti oštećen tokom rada. To će uzrokovati lomljenje žica, što direktno utječe na vijek trajanja konopa čelične žice.
Ako je žičano uže od nehrđajućeg čelika preopterećeno, to će brzo povećati stupanj deformacije stiskanja, a stupanj habanja između unutarnje čelične žice i vanjske čelične žice i odgovarajućeg utora kotača donijet će ozbiljnu štetu sigurnosti rada i skratiti vijek trajanja remenice.